High Hardness Alumina Based Ceramics Insulation Rings ISO14001

Name: High Hardness Alumina Based Ceramics Insulation Rings ISO14001
Brand: Antaeus
Price: 1 USD

Brand Name : Antaeus

Model Number : AD-B018

Certification : /

Place of Origin : Hunan,China

MOQ : Negotiation

Price : Negotiation

Payment Terms : T/T or Negotiation

Supply Ability : Full Supply

Delivery Time : 15-45 days

Packaging Details : Inner vacuum packaging, outside carton.

Product Name : Metallized Alumina Ceramic Rings / Ceramic Insulators for Battery

Material : Alumina (Aluminum Oxide, Al2O3)

Insulation Resistance : 1000M Ω（1000VDC)

High Light : Alumina Ceramic Rings / Metallized Ceramic Insulators / Electrical Ceramic Components

Thermal Shock Resistance room temperature to 850C : will not burst or leak after five operations

Max. Use Temp. : 1650℃

ROHS Hardness : ≥89

Flexural strength : 550 Mpa(psix10^3)

Compressive Strength : 2600(377) Mpa(psix10^3)

Coefficient of thermal expansion : 8.2 X10^-6/℃

Coefficient of thermal conductivity : 17-30.4 W/m.K

Contact Now

Alumina Seal Ceramic Rings / Industry Insulation Rings

1. Description:

Raw material processing of ceramic seal rings:

Milling --- In this process, a raw material is given a desired small shape. Milling of a raw material has different sub-stages, which include destructing, compressing and impacting.

Batching --- In this process, a raw material is given a desired small shape. Milling of a raw material has different sub-stages, which include destructing, compressing and impacting.

Mixing --- In this step, the ceramic ingredients are mixed through various procedures and machines. Often, they are turned into slurries through the addition of water or another liquid additive.

2. Feature Advantages:

1) Refractory, High Temperature Resistance, Maximum Used Temperature: 1800 ºC (3272ºF)
2) Hardness Strength, Wear Resistance Up To Mohz 9.0 ; HRA 80-90
3) High Voltage, Good Insulation Performance ,Electrical Resistivity Up To 10∧14 Ohm.Cm
4) High Polished Surface Up To Rz0.8(Ra0.1)
5) Superior Mechanical Strength, MAX 10 MPa.m1/2 Fracture toughness
6) Pressure Resistance, Max 2300MPa compressive strength
7) Anti-High Corrosion Resistance, Such As Acid Alkali Resistance
8) Long Service Life
9) Other excellent property

3. Material Features / Properties:

Composite	(wt %)	99%	99.5%	99.8%
Color		White or Ivory	White or Ivory	White or Ivory
Density	g/cm 3	3.82	3.9	3.92
Hardness	HRA	83	85	85
Flexural Strength	Mpa (psi*10 3 )	375	386	381

4. Technical Parameters:

Technical Parameters of Ceramics
Items	Test Conditions	Unit or Symbol	99% AL2O3	95% AL2O3	90% AL2O3	Zirconia	Steatite	Silicon Carbide
Volume Density	--	g/cm3	≥3.70	≥3.62	≥3.40	≥5.90	≥2.60	≥3.08
Tightness	--	Pa·m³/s	≤1.0×10-11	≤1.0×10-11	≤1.0×10-11	-	-	-
Liquid Permeability	--	--	Pass	Pass	Pass		Pass	-
Flexural Strength	-	MPa	≥300	≥280	≥230	≥1100	≥120	≥400
Elastic Modulus	-	GPa	-	≥280	≥250	≥220	-	400
Poisson Ratio	-	-	-	0.20～0.25	0.20～0.25	-	-	-
Thermal Shock Resistance	800℃( Room Temperature) Cycle: 10 times		Pass	Pass	Pass	-	-	-
Coefficient of Linear Expansion	20℃～100℃	×10-6 K-1	-	-	-		≤8	-
	20℃～500℃	×10-6 K-1	6.5～7.5	6.5～7.5	6.5～7.5	6.5～11.2	-	-
	20℃～800℃	×10-6 K-1	6.5～8.0	6.5～8.0	6.3～7.3		-	4
	20℃～1200℃	×10-6 K-1	-	7.0～8.5	-	-	-	-
Coefficient of Thermal Conductivity	20℃	W/(m·k)	-	-	-	-	-	90～110
Coefficient of Thermal Conductivity	1000℃	W/(m·k)	-	-	-	-	-	90～110
Dielectric Constant	1MHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	≤7.5	-
	1MHz 50℃	-	-	9.0～10	-	-	-	-
	10GHz 20℃	-	9.0～10.5	9.0～10	9.0～10	-	-	-
Volume Resistivity	100℃	Ω·cm	≥1.0×1013	≥1.0×1013	≥1.0×1013	-	≥1.0×1012	-
	300℃		≥1.0×1013	≥1.0×1010	≥1.0×1013	-	-	-
	500℃		≥1.0×109	≥1.0×108	--	-	-	-
Disruptive Strength	D.C	kV/mm	≥17	≥15	≥15	-	≥20	-
Chemical Durability	1:9HCl	mg/c㎡	≤0.7	≤7.0	-	-	-	-
Chemical Durability	10%NaOH	mg/c㎡	≤0.1	≤0.2	-	--	-	-
Grain Size	-	μm	-	3~12	-	-	-	-

5. Process Flows:

Formulating --- Granulating --- Forming --- Sintering --- Grinding --- Printing --- Nickel Plating --- Assembing --- Brazing --- Inspecting --- Packing